PA6 Resin
SINOPEC Baling PA6 YH800 Nylon 6 Resin | Medium Viscosity Virgin Pellets
SINOPEC Baling YH800 virgin PA6 (nylon 6) resin. Medium viscosity (RV 2.85), natural milky-white pellets for injection molding, monofilament & FR modification. TDS/COA, 25kg bags.
SINOPEC Baling YH800 Virgin PA6 (Nylon 6) Resin — Medium Viscosity Molding Grade
Product Overview：
YH800 is a medium-viscosity virgin polyamide 6 (PA6 / Nylon 6) resin produced by SINOPEC Baling Petrochemical (Yuehua Brand) in Yueyang, Hunan — one of China's largest and most established caprolactam-to-nylon integrated production bases, and a long-standing benchmark PA6 supplier for domestic and export markets.
This natural-color grade features relative viscosity 2.85±0.03, low extractables (<0.5%) and moisture <0.07% , combining good flowability with balanced mechanical performance (tensile 60.7 MPa, flexural modulus 2087 MPa). It is designed for general injection molding, flame-retardant compounding base resin, and monofilament/brown-fiber spinning. LEMA supplies genuine SINOPEC Baling YH800 in original 25kg bags with full TDS/COA.
Key Features：
Medium viscosity, versatile — RV 2.85±0.03, suitable for both injection molding and monofilament spinning
Balanced mechanics — tensile 60.7 MPa, flexural strength 86.6 MPa, flexural modulus 2087 MPa
Good toughness — notched Izod 20.1 kJ/m² (dry as molded), typical PA6 wear & chemical resistance
Low monomer & moisture — extractables <0.5%, moisture <0.07%, fewer bubbles/silver marks
Natural milky-white color — uniform pellets, grade-1 whiteness, excellent base for dyeing or FR/GF modification
Cost-effective — China's flagship volume PA6 grade, stable supply and consistent batch quality
Typical Applications：
Industry | Applications |
|---|---|
General Injection Molding | Housings, brackets, connectors, appliance parts, daily consumer goods |
Monofilament / Fiber | Brown filament, monofilament, bristles, fishing-net yarn, industrial yarn |
FR & Alloy Compounding | Base resin for flame-retardant PA6, PA6/PP alloys, modified compounds |
Automotive | Interior panels, clips, fasteners, non-load-bearing functional parts |
E&E | Switch brackets, cable channels, equipment housings, electrical accessories |
Typical Properties
Property | Test Method | Value | Unit |
|---|---|---|---|
Physical | | | |
Density | GB/T 1033 | 1.156 | g/cm³ |
Relative Viscosity | GB/T 1632 | 2.85±0.03 | — |
Melt Flow Rate (230°C/2.16kg ref.) | GB/T 3682 | ~38 | g/10min |
Moisture Content | FZ/T 51004 | <0.07 | % |
Extractables (residual monomer) | FZ/T 51004 | <0.5 | % |
Mold Shrinkage | GB/T 1043 | 0.93 | % |
Mechanical | | | |
Tensile Strength | GB/T 1040 | 60.7 | MPa |
Elongation at Break | GB/T 1040 | 48.1 | % |
Flexural Strength | GB/T 9341 | 86.6 | MPa |
Flexural Modulus | GB/T 9341 | 2,087 | MPa |
Notched Izod Impact | GB/T 1043 | 20.1 | kJ/m² |
Rockwell Hardness (R) | GB/T 9342 | 72.2 | — |
Thermal | | | |
Melting Point | — | 215–220 | °C |
Heat Deflection Temp (1.82 MPa) | GB/T 1634 | 71 | ° |
Packaging & Shipping：
Item | Details |
|---|---|
Packaging | 25 kg/bag, original SINOPEC Baling bags |
Container Load | 20GP: ~17 MT / 40HQ: 25–27 MT |
MOQ | 1×20'FCL (trial orders negotiable) |
Lead Time | 5working days after deposit |
Storage | Cool, dry, sealed — nylon absorbs moisture |