EVA Resin
EVA Y2022 (14-2) EVA Copolymer Resin | 14% VA Film Grade
EVA Y2022 (14-2) copolymer resin with 14% vinyl acetate, MFR 2 g/10 min and density 0.935 g/cm³. Transparent EVA pellets for blown film, foam and injection molding.
EVA Y2022 (14-2) EVA Copolymer Resin — 14% VA, MFR 2 g/10 min
EVA Y2022 (14-2) is a transparent ethylene vinyl acetate copolymer resin supplied in pellet form. This Beijing Organic EVA grade has a reported vinyl acetate content of 14%, melt flow rate of 2 g/10 min and density of 0.935 g/cm³.
Designed for buyers sourcing EVA pellets for film, foam and injection-molded applications, EVA Y2022 (14-2) can be evaluated for blown film, industrial film, agricultural film, foam products and molded parts.
Key Features
- Transparent EVA copolymer resin in pellet form
- Reported 14% vinyl acetate content
- Reported MFR: 2 g/10 min
- Suitable for blown film, foam molding and injection molding
- Reported low haze and good gloss characteristics
- Available for B2B resin sourcing and technical evaluation
Typical Technical Data
Property | Reported Value | Test Method |
|---|---|---|
Melt Flow Rate (MFR) | 2 g/10 min | ASTM D1238 |
Density | 0.935 g/cm³ | ASTM D1505 |
Vinyl Acetate Content | 14% | ISO DIS 8965/1989(E) |
Tensile Yield Strength, Transverse | 4.1 N/mm² | ASTM D638 |
Tensile Yield Strength, Longitudinal | 4.5 N/mm² | ASTM D638 |
Tensile Break Strength, Transverse | 24 N/mm² | ASTM D638 |
Tensile Break Strength, Longitudinal | 24 N/mm² | ASTM D638 |
Elongation at Break, Transverse | 720% | ASTM D6398 |
Elongation at Break, Longitudinal | 440% | ASTM D6398 |
Shore D Hardness | 33 | ASTM D2240 |
Shore A Hardness | 92 | ASTM D2240 |
Melting Point | 95°C | Internal method |
Vicat Softening Temperature | 70°C | ASTM D1525 |
Haze | 1.9% | Reported value |
Gloss | 82% | Reported value |
EVA Resin for Blown Film
With its reported 14% VA content and transparent appearance, EVA Y2022 (14-2) can be assessed for blown-film production. Reported application areas include agricultural film, industrial film and film-related converting projects.
For processors, confirm formulation, thickness, processing window and finished-film requirements with trial material before commercial production.
EVA Resin for Foam and Injection Molding
This EVA copolymer resin is also reported for foam molding and injection molding. EVA pellets may be evaluated for flexible foam articles and molded components where the grade’s balance of flow, clarity and mechanical properties is relevant.
Processing conditions should be optimized according to equipment, mold design, additive package and final-product requirements.
Product Identification
This grade may be referenced in sourcing documents using several common variants:
- EVA Y2022 (14-2)
- EVA Y2022 14-2
- EVA Y2022(14-2)
- EVA Y2022 142
- EVA resin 14 VA
Including these variants helps purchasing teams match RFQs, packing lists and product specifications accurately.